Code

Copper

C77000 Copper

Grade Designation & Standards

Standard Grade: C77000 (Nickel Silver/German Silver)

International Equivalents:

UNS: C77000 (ASTM B122, B151, B206)
EN: CW410J (DIN 17663), CuNi18Zn27
JIS: C7701

Applicable Standards:

GB/T 4423-1992 (China)
ASTM B122 (USA)
EN 12163 (Europe)

Product Features

1. High Strength & Corrosion Resistance: Tensile strength ≥440 MPa (hard state), resistant to seawater, weak acids, and high-temperature oxidation (corrosion rate ≤0.003 mm/a).

2. Excellent Machinability: Good cold/hot working performance with surface finish up to Ra 0.1μm; poor weldability requiring special processes.

3. Aesthetic & Functional: Silver-white appearance for decorative and industrial applications.

4. Temperature Adaptability: Operates reliably from -100°C to 300°C with no low-temperature embrittlement.

Common Product Forms & Dimensions

Product Form	Size Range	Delivery Condition
Sheet	Thickness: 0.05-1.5mm, Width ≤500mm	Soft (M), Hard (H)
Rod	Diameter: 3-120mm, Length: 2-6m	Drawn, Hot-Rolled
Tube	OD: 2-150mm, Wall Thickness: 0.3-15mm	Cold-Drawn, Half-Hard
Wire	Diameter: 0.05-6.0mm	Coiled or Straight
Strip	Thickness: 0.1-3.0mm	Custom Cut
(Data sources: Consistent across multiple references)

Chemical Composition

Element	Content (%)	Function/Limit
Cu	62.0-65.0	Base material, corrosion resistance & conductivity
Ni+Co	13.5-16.5	Enhances corrosion resistance & strength
Zn	Balance	Adjusts plasticity, reduces cost
Pb	≤0.02	Strictly controlled
Fe	≤0.5	Trace impurities
Mn	≤0.3	Improves machinability
(Data sources: Consistent across multiple references)

Physical Properties

Property	Value	Remarks
Density	8.70-8.75 g/cm³	High density for precision parts
Electrical Conductivity	5.7-6% IACS	Moderate conductivity for industrial use
Thermal Conductivity	18-33 W/(m·K)	Moderate heat dissipation
Thermal Expansion	17.2×10⁻⁶/°C (20-300°C)	Excellent thermal stability
Melting Point	900-1100°C	Limited castability
(Data sources: Integrated from multiple references)

Mechanical Properties

Property	Soft (M)	Hard (H)
Tensile Strength (σb)	350-450 MPa	640-730 MPa
Yield Strength (σ0.2)	105-250 MPa	≥600 MPa
Elongation (δ10)	20-40%	3-9%
Vickers Hardness (HV)	80-130	200-230
(Values vary slightly depending on product form and state)

Core Advantages

1. Balanced Performance: Combines high strength, corrosion resistance, and wear resistance for harsh environments.

2. Machining Flexibility: Supports cold/hot rolling and stamping with high surface finish.

3. Cost-Efficiency: Lower cost than high-nickel alloys (e.g., C71500) with comparable performance.

Product Applications

1. Marine Engineering: Ship propellers, seawater valves, offshore platform components.

2. Chemical Equipment: Corrosion-resistant pipes, pump bodies, reactor linings.

3. Mechanical Engineering: Gears, bearings, high-load connectors.

4. Aerospace: Engine components, hydraulic system pipelines.

5. Electrical Engineering: Connectors, heat sinks.

Processing Guidelines

1. Welding: Prefer TIG or laser welding; interpass temperature ≤100°C to avoid zinc evaporation.

2. Annealing: Post-cold working, anneal at 650-750°C; hot working temperature: 950-970°C.

3. Machining: Cutting speed ≤50 m/min; use carbide tools with oil-based coolant.

Key Application Scenarios

High-Temperature & High-Pressure Systems: Petrochemical valves, nuclear reactor seals.
Precision Machinery: Aerospace components, medical device wear parts.

FAQs

1. Q: How does C77000 differ from brass?

A: C77000 offers superior corrosion resistance and strength but at a higher cost.

2. Q: Is it suitable for strong acid environments?

A: Suitable for weak acids and seawater but avoid strong oxidizing acids (e.g., nitric acid).

3. Q: Post-weld heat treatment required?

A: Recommend low-temperature annealing (250-300°C) to eliminate residual stress.

Standard References

Chemical Composition: GB/T 4423-1992, ASTM B122.
Mechanical Testing: EN 12163, ASTM B206.
Processing: ISO 426-2, Aerospace Standard AMS 4590.

Note: Data consolidated from industrial standards and technical documents. Actual parameters may vary slightly due to manufacturing processes. Refer to supplier test reports for precise specifications.