C26800 Brass

Grade Name

• UNS Number: C26800

• Common Name: Yellow Brass (65% Cu, 34% Zn)

• Corresponding Standards: ASTM B36/B36M (Brass Sheet/Strip), ASTM B134 (Brass Wire), SAE J463.

Product Features

• Excellent Cold Formability: Ideal for deep drawing, stamping, and bending.

• High Strength and Ductility: Balanced mechanical properties for structural applications.

• Good Corrosion Resistance: Suitable for indoor and mild outdoor environments.

• Cost-Effective Manufacturing: Optimized for high-volume production.

• Aesthetic Appeal: Bright yellow finish for decorative and architectural uses.

Common Product Forms & Dimensions

Form	Thickness (mm)	Width (mm)	Length (mm)	Diameter (mm)
Sheet/Strip	0.2 – 6.0	50 – 600	Custom	–
Rod/Bar	–	–	Custom	3 – 50
Wire	–	–	Custom	0.3 – 12
Tube	1 – 12 (wall)	–	Custom	10 – 150 (OD)
Note: Custom dimensions are available upon request.

C26800 Chemical Composition

Element	Cu	Zn	Pb	Fe	Others
Weight %	64–68.5	Balance	≤0.07	≤0.05	≤0.15
Complies with ASTM B36 and SAE J463 standards.

Physical Properties

Property	Value
Density (g/cm³)	8.45–8.55
Melting Point (°C)	900–930
Electrical Conductivity (%IACS)	25–28 (Annealed)
Thermal Conductivity (W/m·K)	105–120 (at 20°C)
Values may vary depending on processing conditions.

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength (MPa)	Elongation (%)	Hardness (HV)
Annealed	270–350	90–130	50–65	55–75
Cold Worked (H02)	400–500	320–380	20–30	100–130
Cold Worked (H04)	500–600	450–520	5–10	150–180
Data applies to standard thicknesses and processing states.

Core Advantages

1. Superior Formability: Perfect for complex stamped or drawn components.

2. Cost Efficiency: Lower copper content reduces material costs.

3. Decorative Versatility: Bright yellow color ideal for architectural accents.

4. Environmental Resistance: Resists tarnishing in humid conditions.

Product Applications

• Decorative: Architectural trim, door handles, and lighting fixtures.

• Electronics: Connectors, terminals, and shielding components.

• Plumbing: Low-pressure fittings and valve bodies.

• Automotive: Radiator cores, fuel system parts.

• Industrial: Fasteners, springs, and stamped hardware.

Processing Considerations

• Annealing: 425–600°C to restore ductility after cold working.

• Machining: Use sharp tools with lubricants to prevent material adhesion.

• Welding: Compatible with TIG and resistance welding; minimize heat input to avoid zinc depletion.

• Surface Finishing: Electroplating or clear coating recommended for decorative applications.

Key Application Scenarios

• Architectural projects requiring corrosion-resistant decorative elements.

• High-volume production of stamped automotive components.

• Consumer electronics with aesthetic design requirements.

• HVAC and plumbing systems in residential buildings.

FAQs

Q1: How does C26800 differ from C26000 brass?

A: C26800 has lower copper content (65% vs. 70%) than C26000, offering reduced cost but slightly lower strength and conductivity.

Q2: Is C26800 suitable for marine environments?

A: Limited to freshwater or low-salinity applications; protective coatings are recommended for saltwater exposure.

Q3: Can C26800 be recycled?

A: Yes, it is fully recyclable and aligns with sustainable manufacturing practices.

Standard References

Standard	Description
ASTM B36/B36M	Specifications for brass sheet, strip, and rolled bar.
ASTM B134	Standard for brass wire.
SAE J463	Mechanical property standards for wrought copper alloys.

Note: Specifications may vary slightly depending on manufacturer and processing methods. Always consult technical datasheets for critical applications.